Penyelam amatir idealnya punya jam tangan yg bagus, jika memang masih sayang sama nyawa dia, dan hendaknya jangan cuek bebek untuk mencari jam diving sesuai kriteria yg memadai. Masalahnya, banyak yg tidak nyaman dengan bentuk jam diving yg dicap terlalu besar, bulky, gede banget bak meteran air, gak manis tampilannya. Apalagi buat diver cewe, mereka biasanya gak suka pakai jam diving karena alasan breed asli jam diving memang sangat "berselera cowo", tangan cewe seakan tenggelam habis oleh besarnya lingkar diameter jam dan ketebalannya. Namun kembali lagi soal safety, bahwa jam diving yg sangat baik itu perlu buat penyelam amatir karena salah satu keselamatan dia ada dijam itu, tinggal pilih sayang nyawa atau malahan ribet ngurusin bentuk jam yg gede.
Jam khusus diving pro mempunyai standar ISO 2281 dan ISO 6425 agar dikatakan "sangat layak dipakai buat diving". Dipasaran banyak dijual jam dengan kemasan spt jam diving hanya karena seenaknya diberi label "diver watch", atau karena gembar gembor marketingnya yg melambung kelangit menyebut jam itu untuk olahraga air dan diving dengan mencantumkan tulisan di-dials nya : Water Proof 100m.
Tampangnya sih bergaya diver, tapi jika dikupas satu persatu ternyata jam itu sama sekali tidak memenuhi standar ISO 2281 dan 6425. Saya pernah satu waktu suka dengan "jam diving banci" karena terpengaruh dengan designnya yg menarik. Bosan dengan jam diving yg begitu begitu saja, akhirnya menolehkan kepala melihat ke jam diving dengan tema fashion, salah satunya yg dibeli adalah GUESS water steel pro, lihat foto sebelah. Bentuknya sih keren, bergaya habisssss ala diver plus imbuhan WR 10 bar, tapi ini sama sekali gak masuk memenuhi kriteria ISO buat jam diving. Gagalnya dia masuk dalam kriteria ISO jam diving al: bodinya mudah gores tidak alot, lalu penunjuk angkanya tidak diberi cat lume yg cukup kuat (sejenis fosfor yg bisa menyala sehabis terkena sinar matahari) agar bisa dilihat dalam kegelapan total selama sekian jam. Guess itu lumenya hanya menyala 15 menitan saja setelah itu mati, waduuuuh. Lume yg kuat adalah syarat mutlak buat jam diving. Membandingkan dengan lume dideretan jam diving profesional lansiran dari Seiko yg bisa menyala 7-10 jam, jelas jam Guess diving ini dikatakan jelek. Guess water steel pro yg dibeli tahun 2003 ini masih disimpan sampai skr dan kadang dipakai buat berenang ringan dikolam renang.
SALE:
http://hsgautama.blogspot.com/search/label/A-SALE
SALE LORUS scuba diver style "warna permen lolipop"
http://hsgautama.blogspot.com/2013/03/sale-lorus-scuba-diver-style-warna.html
BAG 2 bagaimana memilih jam diving yang sesuai:
http://hsgautama.blogspot.com/2012/08/bagaimana-memilih-jam-diving-yg-sesuai.html
Penjelasan standar ISO buat jam diving dikutip dari WIKI
ISO 2281 water-resistant watches standard
The International Organization for Standardization issued a standard for water resistant watches which also prohibits the term waterproof to be used with watches, which many countries have adopted. The international standard ISO 2281 Horology – Water-resistant watches defines the water resistance of watches. This standard was only designed for watches intended for ordinary daily use and are resistant to water during exercises such as swimming for a short period. They may be used under conditions where water pressure and temperature vary. However, whether they bear an additional indication of overpressure or not, they are not intended for submarine diving.
The ISO 2281 standard specifies a detailed testing procedure for each mark that defines not only pressures but also test duration, water temperature, and other parameters. Besides this ISO 2859-2 Sampling plans indexed by limiting quality (LQ) for isolated lot inspection and ISO 2859-3 Sampling procedures for inspection by attributes – Part 3: Skip-lot sampling procedures concerning procedures regarding lot sampeling testing come into play, since not every single watch has to be tested for ISO 2281 approval.
ISO 2281 water resistance testing of a watch consists of:
Resistance when immersed in water at a depth of 10 cm. Immersion of the watch in 10 cm of water for 1 hour.
Resistance of operative parts. Immersion of the watch in 10 cm of water with a force of 5 N perpendicular to the crown and pusher buttons (if any) for 10 minutes.
Condensation test. The watch shall be placed on a heated plate at a temperature between 40 °C and 45 °C until the watch has reached the temperature of the heated plate (in practice, a heating time of 10 minutes to 20 minutes, depending on the type of watch, will be sufficient). A drop of water, at a temperature of 18 °C to 25 °C shall be placed on the glass of the watch. After about 1 minute, the glass shall be wiped with a dry rag. Any watch which has condensation on the interior surface of the glass shall be eliminated.
Resistance to different temperatures. Immersion of the watch in 10 cm of water at the following temperatures for 5 minutes each, 40 °C, 20 °C and 40 °C again, with the transition between temperatures not to exceed 1 minute. No evidence of water intrusion or condensation is allowed.
Resistance to air overpressure. Exposing the watch to an overpressure of 2 bar. The watch shall show no air-flow exceeding 50 μg/min.
No magnetic or shock resistance properties are required.
No negative pressure test is required.
No strap attachment test is required.
No corrosion test is required.
Except the thermal shock resistance test all further ISO 2281 testing should be conducted at 18 °C to 25 °C temperature. Regarding pressure ISO 2281 defines: 1 bar = 105 Pa = 105 N/m2.
In practice, the survivability of the watch will depend not only on the water depth, but also on the age of the sealing material, past damage, temperature, and additional mechanical stresses.
None of the tests defined by ISO 2281 are suitable to qualify a watch as a diving watch. ISO 2281 compliant watches are designed for everyday life and must be water resistant during exercises such as swimming for a short period. They can be worn in different temperature and pressure conditions but are under no circumstances designed for diving with underwater breathing apparatus.
The standards and features for diving watches are regulated by the ISO 6425 - Divers' watches international standard. ISO 6425 defines such watches as: A watch designed to withstand diving in water at depths of at least 100 m and possessing a system to control the time. Diving watches are tested in static or still water under 125% of the rated (water)pressure, thus a watch with a 200 meter rating will be water resistant if it is stationary and under 250 meters of static water. The testing of the water resistance is fundamentally different from non-dive watches, because every watch has to be fully tested.
ISO 6425 water resistance testing of a diver's watch consists of:
Reliability under water. The watches under test shall be immersed in water to a depth of 30 cm ± 2 cm for 50 hours at 18 °C to 25 °C and all the mechanisms shall still function correctly. The condensation test shall be carried out before and after this test to ensure that the result is related to the above test.
Condensation test. The watch shall be placed on a heated plate at a temperature between 40 °C and 45 °C until the watch has reached the temperature of the heated plate (in practice, a heating time of 10 minutes to 20 minutes, depending on the type of watch, will be sufficient). A drop of water, at a temperature of 18 °C to 25 °C shall be placed on the glass of the watch. After about 1 minute, the glass shall be wiped with a dry rag. Any watch which has condensation on the interior surface of the glass shall be eliminated.
Resistance of crowns and other setting devices to an external force. The watches under test shall be subjected to an overpressure in water of 125% of the rated pressure/10 bar for 10 minutes and to an external force of 5 N perpendicular to the crown and pusher buttons (if any). The condensation test shall be carried out before and after this test to ensure that the result is related to the above test.
Water-tightness and resistance at a water overpressure. The watches under test shall be immersed in water contained in a suitable vessel. Then an overpressure of 125% of the rated pressure shall be applied within 1 minute and maintained for 2 hours. Subsequently the overpressure shall be reduced to 0.3 bar within 1 minute and maintained at this pressure for 1 hour. The watches shall then be removed from the water and dried with a rag. No evidence of water intrusion or condensation is allowed.
Resistance to thermal shock. Immersion of the watch in 30 cm ± 2 cm of water at the following temperatures for 10 minutes each, 40 °C, 5 °C and 40 °C again. The time of transition from one immersion to the other shall not exceed 1 min. No evidence of water intrusion or condensation is allowed.
An optional test originating from the ISO 2281 tests (but not required for obtaining ISO 6425 approval) is exposing the watch to an overpressure of 2 bar. The watch shall show no air-flow exceeding 50 μg/min.
Except the thermal shock resistance test all further ISO 6425 testing should be conducted at 18 °C to 25 °C temperature. Regarding pressure ISO 6425 defines: 1 bar = 105 Pa = 105 N/m2. The required 125% test pressure provides a safety margin against dynamic pressure increase events, water density variations (seawater is 2 to 5% denser than freshwater) and degradation of the seals.
Movement induced dynamic pressure increase is sometimes the subject of urban myths and marketing arguments for diver's watches with high water resistance ratings. When a diver makes a fast swimming movement of 10 m/s (32.8 ft/s) (the best competitive swimmers and finswimmers do not move their hands nor swim that fast[1]) physics dictates that the diver generates a dynamic pressure of 0.5 bar or the equivalent of 5 meters of additional water depth.[2]
Besides water resistance standards to a minimum of 100 metres (330 ft) depth rating ISO 6425 also provides minimum requirements for mechanical diver's watches (quartz and digital watches have slightly differing readability requirements) such as:[3]
The presence of a time-preselecting device, for example a unidirectional rotating bezel or a digital display. Such a device shall be protected against inadvertent rotation or wrong manipulation. If it is a rotating bezel, it shall have a minute scale going up to 60 min. The markings indicating every 5 min shall be clearly indicated. The markings on the dial, if existing, shall be coordinated with those of the preselecting device and shall be clearly visible. If the preselecting device is a digital display, it shall be clearly visible.
The following items of the watch shall be legible at a distance of 25 cm (9.8 in) in the dark:
time (the minute hand shall be clearly distinguishable from the hour hand);
set time of the time-preselecting device;
indication that the watch is running (This is usually indicated by a running second hand with a luminous tip or tail.);
in the case of battery-powered watches, a battery end-of-life indication.
The presence of an indication that the watch is running in total darkness. This is usually indicated by a running second hand with a luminous tip or tail.
Magnetic resistance. This is tested by 3 expositions to a direct current magnetic field of 4,800 A/m. The watch must keep its accuracy to +/- 30 seconds/day as measured before the test despite the magnetic field.
Shock resistance. This is tested by two shocks (one on the 9 o'clock side, and one to the crystal and perpendicular to the face). The shock is usually delivered by a hard plastic hammer mounted as a pendulum, so as to deliver a measured amount of energy, specifically, a 3 kg hammer with an impact velocity of 4.43 m/s. The change in rate allowed is +/- 60 seconds/day.
Resistance of attachments to an external force (strap/band solidity). This is tested by applying a force of 200 N (45 lbf) to each springbar (or attaching point) in opposite directions with no damage to the watch of attachment point. The bracelet of the watch being tested shall be closed.
Marking. Watches conforming to ISO 6425 are marked with the word DIVER’S WATCH L M or DIVER'S L M to distinguish diving watches from look a like watches that are not suitable for actual scuba diving. The letter L indicates the diving depth, in metres, guaranteed by the manufacturer.
Diver’s watches for mixed-gas diving
Diving at a great depth and for a long period is done in a diving chamber, with the diver spending time alternately in the water and in a pressurized environment, breathing a gas mixture. In this case, the watch is subjected to the pressure of the gas mixture and its functioning can be disturbed. Consequently, it is recommended to subject the watch to a special extra test. ISO 6425 defines a diver’s watch for mixed-gas diving as: A watch required to be resistant during diving in water to a depth of at least 100 m and to be unaffected by the overpressure of the mixed gas used for breathing.
The following specific additional requirements for testing of diver's watches for mixed-gas diving are provided by ISO 6425:
Test of operation at a gas overpressure. The watch is subject to the overpressure of gas which will actually be used, i.e. 125% of the rated pressure, for 15 days. Then a rapid reduction in pressure to the atmospheric pressure shall be carried out in a time not exceeding 3 minutes. After this test, the watch shall function correctly. An electronic watch shall function normally during and after the test. A mechanical watch shall function normally after the test (the power reserve normally being less than 15 days).
Test by internal pressure (simulation of decompression). Remove the crown together with the winding and/or setting stem. In its place, fit a crown of the same type with a hole. Through this hole, introduce the gas mixture which will actually be used and create an overpressure of the rated pressure/20 bar in the watch for a period of 10 hours. Then carry out the test at the rated water overpressure. In this case, the original crown with the stem shall be refitted beforehand. After this test, the watch shall function correctly.
Marking. Watches used for mix-gas diving which satisfy the test requirements are marked with the words "DIVER’S WATCH L M FOR MIXED-GAS DIVING". The letter L indicates the diving depth, in metres, guaranteed by the manufacturer. The composition of the gas mixture used for the test shall be given in the operating instructions accompanying the watch.
Most manufacturers recommend divers to have their diving watch pressure tested by an authorized service and repair facility annually or every two to three years and have the seals replaced.
** Koleksi album tahun 1988-97
No comments:
Post a Comment
PERHATIAN :::::::::::
* Komentar DI MODERASI oleh admin dengan persetujuan.
* Komentar HANYA soal isi blog ini saja. Promo dilarang disini, maaf.
* Jika kalian penipu online, fake onlineshop jangan harap bisa posting disini. Blog ini tidak dipakai buat numpang aksi penipuan oleh pihak lain. Carilah makan halal sana dan jangan menipu.
* NO offensive item, NO haters gak jelas, NO kekerasan, NO SARA, NO Sex item whatsoeva, NO Judi online, NO drugs, NO Alcohol, NO praktek dukun mistik dan pesugihan.